The reliability of microelectronic components is profoundly influenced by the fracture resistance of the polymer/inorganic interfaces and by the progressive debonding of these interfaces in aqueous environments. Consequently, fatigue (slow) crack growth in epoxy/glass interfaces bonded with the silane coupling agent 3-aminopropyltriethoxysilane (3-APES) was studied under static and cyclic loading at 23°C and in either dry or humid conditions using the double cleavage drilled compression (DCDC) test. Crack growth rates under cyclic loading were significantly greater than under static loading, indicating that stress corrosion effects are negligible and that crack tip plasticity controls cyclic fatigue crack growth at silane (3-APES) bonded epoxy/glass interfaces. After aging at 94°C in water, these silane bonded epoxy/glass interfaces exhibited somewhat greater resistance to cyclic fatigue crack growth than the unaged samples; however, after aging at 98°C in water cyclic fatigue crack growth became cohesive and fractal in nature. Mechanisms for fatigue crack growth at silane (3-APES) bonded epoxy/glass interfaces are discussed.
Skip Nav Destination
Article navigation
December 2001
Papers On Reliability
Adhesion and Reliability of Epoxy/Glass Interfaces
John E. Ritter,
John E. Ritter
Mechanical and Industrial Engineering Department, University of Massachusetts, Amherst, MA 01003-2210
Search for other works by this author on:
Armin Huseinovic
Armin Huseinovic
Mechanical and Industrial Engineering Department, University of Massachusetts, Amherst, MA 01003-2210
Search for other works by this author on:
John E. Ritter
Mechanical and Industrial Engineering Department, University of Massachusetts, Amherst, MA 01003-2210
Armin Huseinovic
Mechanical and Industrial Engineering Department, University of Massachusetts, Amherst, MA 01003-2210
Contributed by the Electronic and Photonic Packaging Division for publication in the JOURNAL OF ELECTRONIC PACKAGING. Manuscript received by the EPPD January 3, 2000, Associate Editor: S. M. Heinrich.
J. Electron. Packag. Dec 2001, 123(4): 401-404 (4 pages)
Published Online: January 3, 2000
Article history
Received:
January 3, 2000
Citation
Ritter , J. E., and Huseinovic, A. (January 3, 2000). "Adhesion and Reliability of Epoxy/Glass Interfaces ." ASME. J. Electron. Packag. December 2001; 123(4): 401–404. https://doi.org/10.1115/1.1388560
Download citation file:
Get Email Alerts
Cited By
Enhancing Mechanical Reliability of Silver-Sintered Joints With Copper Nanowires in High-Power Electronic Devices
J. Electron. Packag (December 2024)
Special Issue on InterPACK2023
J. Electron. Packag (December 2024)
Impact of Encapsulated Phase Change Material Additives for Improved Thermal Performance of Silicone Gel Insulation
J. Electron. Packag (December 2024)
Related Articles
Special Issue on Poly’2000, London
J. Electron. Packag (December,2002)
Controlling Subcritical Crack Growth at Epoxy/Glass Interfaces
J. Electron. Packag (December,2002)
On the Mechanical Reliability of Photo-BCB-Based Thin Film Dielectric Polymer for Electronic Packaging Applications
J. Electron. Packag (March,2000)
Interfacial Versus Cohesive Failure on Polymer-Metal Interfaces in Electronic Packaging—Effects of Interface Roughness
J. Electron. Packag (June,2002)
Related Proceedings Papers
Related Chapters
Reliability-Based Inspection Intervals of Offshore Jacket Fleets
Ageing and Life Extension of Offshore Facilities
Surface Analysis of Polymer and Glass
Quantitive Surface Analysis of Materials
Surface Analysis and Tools
Tribology of Mechanical Systems: A Guide to Present and Future Technologies